Magnetic Characteristics of Ni-Filled Luminescent Porous Silicon

Petra Granitzer, Klemens Rumpf, Peter Pölt, Michael Reissner

Publikation: Beitrag in einer FachzeitschriftArtikelForschungBegutachtung

Abstract

The aim of the presented work is to combine luminescent porous silicon (PSi) with a ferromagnetic metal (Ni) to modify on the one hand the photoluminescence by the presence of metal deposits and on the other hand to influence the optical properties by an external magnetic field. The optical properties are investigated especially with respect to the wavelength-shift of the photoluminescence due to the metal filling. With increasing metal deposits within PSi the photoluminescence peak is blue-shifted and furthermore an increase of the intensity is observed. Photoluminescence spectra of bare PSi show a maximum around 620 nm whereas in the case of Ni filled samples the peak is blue-shifted to around 580 nm for a deposition time of 15 min. Field dependent magnetic measurements performed with an applied field parallel and perpendicular to the surface, respectively, show a magnetic anisotropy which is in agreement with a thin film. This film-like behavior is caused by the interconnected Ni structures due to the branched porous silicon morphology. The coercivity increases with increasing metal deposition from about 150 Oe to about 450 Oe and also the magnetic anisotropy is enhanced with the growth of metal deposits. Within this work the influence of the magnetic metal filling on the optical properties and the magnetic characterization of the nanocomposites are discussed. The presented systems give not only rise to optoelectronics applications but also to magneto optical integrated devices.

Originalspracheenglisch
Aufsatznummer41
Seiten (von - bis)41
FachzeitschriftFrontiers in Chemistry
Jahrgang7
DOIs
PublikationsstatusVeröffentlicht - 2019

Fingerprint

Porous silicon
porous silicon
Metals
Photoluminescence
metals
photoluminescence
Deposits
Optical properties
Magnetic anisotropy
deposits
optical properties
magnetic metals
anisotropy
Ferromagnetic materials
Magnetic variables measurement
Coercive force
Optoelectronic devices
magnetic measurement
coercivity
Nanocomposites

Schlagwörter

    ASJC Scopus subject areas

    • !!Condensed Matter Physics
    • !!Chemistry(all)

    Fields of Expertise

    • Advanced Materials Science

    Treatment code (Nähere Zuordnung)

    • Experimental

    Kooperationen

    • NAWI Graz

    Dies zitieren

    Magnetic Characteristics of Ni-Filled Luminescent Porous Silicon. / Granitzer, Petra; Rumpf, Klemens; Pölt, Peter; Reissner, Michael.

    in: Frontiers in Chemistry, Jahrgang 7, 41, 2019, S. 41.

    Publikation: Beitrag in einer FachzeitschriftArtikelForschungBegutachtung

    Granitzer, Petra ; Rumpf, Klemens ; Pölt, Peter ; Reissner, Michael. / Magnetic Characteristics of Ni-Filled Luminescent Porous Silicon. in: Frontiers in Chemistry. 2019 ; Jahrgang 7. S. 41.
    @article{369f2062274a48b785c8e192ead96235,
    title = "Magnetic Characteristics of Ni-Filled Luminescent Porous Silicon",
    abstract = "The aim of the presented work is to combine luminescent porous silicon (PSi) with a ferromagnetic metal (Ni) to modify on the one hand the photoluminescence by the presence of metal deposits and on the other hand to influence the optical properties by an external magnetic field. The optical properties are investigated especially with respect to the wavelength-shift of the photoluminescence due to the metal filling. With increasing metal deposits within PSi the photoluminescence peak is blue-shifted and furthermore an increase of the intensity is observed. Photoluminescence spectra of bare PSi show a maximum around 620 nm whereas in the case of Ni filled samples the peak is blue-shifted to around 580 nm for a deposition time of 15 min. Field dependent magnetic measurements performed with an applied field parallel and perpendicular to the surface, respectively, show a magnetic anisotropy which is in agreement with a thin film. This film-like behavior is caused by the interconnected Ni structures due to the branched porous silicon morphology. The coercivity increases with increasing metal deposition from about 150 Oe to about 450 Oe and also the magnetic anisotropy is enhanced with the growth of metal deposits. Within this work the influence of the magnetic metal filling on the optical properties and the magnetic characterization of the nanocomposites are discussed. The presented systems give not only rise to optoelectronics applications but also to magneto optical integrated devices.",
    keywords = "Magnetic behavior, Magnetic nanostructures, Metal deposition, Photoluminescence, Porous silicon, magnetic behavior, photoluminescence, porous silicon, metal deposition, magnetic nanostructures",
    author = "Petra Granitzer and Klemens Rumpf and Peter P{\"o}lt and Michael Reissner",
    year = "2019",
    doi = "10.3389/fchem.2019.00041",
    language = "English",
    volume = "7",
    pages = "41",
    journal = "Frontiers in Chemistry",
    issn = "2296-2646",
    publisher = "Frontiers Media S. A.",

    }

    TY - JOUR

    T1 - Magnetic Characteristics of Ni-Filled Luminescent Porous Silicon

    AU - Granitzer, Petra

    AU - Rumpf, Klemens

    AU - Pölt, Peter

    AU - Reissner, Michael

    PY - 2019

    Y1 - 2019

    N2 - The aim of the presented work is to combine luminescent porous silicon (PSi) with a ferromagnetic metal (Ni) to modify on the one hand the photoluminescence by the presence of metal deposits and on the other hand to influence the optical properties by an external magnetic field. The optical properties are investigated especially with respect to the wavelength-shift of the photoluminescence due to the metal filling. With increasing metal deposits within PSi the photoluminescence peak is blue-shifted and furthermore an increase of the intensity is observed. Photoluminescence spectra of bare PSi show a maximum around 620 nm whereas in the case of Ni filled samples the peak is blue-shifted to around 580 nm for a deposition time of 15 min. Field dependent magnetic measurements performed with an applied field parallel and perpendicular to the surface, respectively, show a magnetic anisotropy which is in agreement with a thin film. This film-like behavior is caused by the interconnected Ni structures due to the branched porous silicon morphology. The coercivity increases with increasing metal deposition from about 150 Oe to about 450 Oe and also the magnetic anisotropy is enhanced with the growth of metal deposits. Within this work the influence of the magnetic metal filling on the optical properties and the magnetic characterization of the nanocomposites are discussed. The presented systems give not only rise to optoelectronics applications but also to magneto optical integrated devices.

    AB - The aim of the presented work is to combine luminescent porous silicon (PSi) with a ferromagnetic metal (Ni) to modify on the one hand the photoluminescence by the presence of metal deposits and on the other hand to influence the optical properties by an external magnetic field. The optical properties are investigated especially with respect to the wavelength-shift of the photoluminescence due to the metal filling. With increasing metal deposits within PSi the photoluminescence peak is blue-shifted and furthermore an increase of the intensity is observed. Photoluminescence spectra of bare PSi show a maximum around 620 nm whereas in the case of Ni filled samples the peak is blue-shifted to around 580 nm for a deposition time of 15 min. Field dependent magnetic measurements performed with an applied field parallel and perpendicular to the surface, respectively, show a magnetic anisotropy which is in agreement with a thin film. This film-like behavior is caused by the interconnected Ni structures due to the branched porous silicon morphology. The coercivity increases with increasing metal deposition from about 150 Oe to about 450 Oe and also the magnetic anisotropy is enhanced with the growth of metal deposits. Within this work the influence of the magnetic metal filling on the optical properties and the magnetic characterization of the nanocomposites are discussed. The presented systems give not only rise to optoelectronics applications but also to magneto optical integrated devices.

    KW - Magnetic behavior

    KW - Magnetic nanostructures

    KW - Metal deposition

    KW - Photoluminescence

    KW - Porous silicon

    KW - magnetic behavior

    KW - photoluminescence

    KW - porous silicon

    KW - metal deposition

    KW - magnetic nanostructures

    UR - http://www.scopus.com/inward/record.url?scp=85061201277&partnerID=8YFLogxK

    U2 - 10.3389/fchem.2019.00041

    DO - 10.3389/fchem.2019.00041

    M3 - Article

    VL - 7

    SP - 41

    JO - Frontiers in Chemistry

    JF - Frontiers in Chemistry

    SN - 2296-2646

    M1 - 41

    ER -