Crack detectability and durability of coaxial cable sensors in reinforced concrete bridge applications

Genda Chen, Ryan McDaniel, Michael Brower, David Pommerenke

Research output: Contribution to journalArticleResearchpeer-review

Abstract

The working mechanism and the measurement principle of topologybased crack sensors made of coaxial cables are briefly reviewed. The sensitivity, spatial resolution, and ruggedness of two coaxial cable sensors, respectively made of rubber and Teflon dielectric materials, were compared and validated with laboratory testing of a 4/5-scale, T-shaped, reinforced concrete beam-column specimen. Two Teflon sensors were installed on one of the solid decks of a three-span continuous highway bridge to investigate their durability and measurement repeatability. Laboratory tests indicated that both types of sensors have high sensitivity, but the Teflon sensor has a higher spatial resolution and a negligible spillover effect of any significant cracks. At a 90-degree bend, however, the Teflon sensor is more susceptible than the rubber sensor to the rubbing action of the outer conductor of a coaxial cable against its dielectric layer. No cracks were observed during the field load tests of the instrumented bridge. Both sensors indicated high durability in realworld application but a certain variation of waveforms was measured over a period of 5 years because of the use of different instruments. Future research is directed to develop an online calibration of crack sensors with a small portion of built-in standard cable at the end of the cable sensor.

Original languageEnglish
Pages (from-to)151-156
Number of pages6
JournalTransportation Research Record
Issue number2172
DOIs
Publication statusPublished - 12 Jan 2010
Externally publishedYes

ASJC Scopus subject areas

  • Civil and Structural Engineering
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Crack detectability and durability of coaxial cable sensors in reinforced concrete bridge applications'. Together they form a unique fingerprint.

  • Cite this