Thermo-mechanical Fatigue Behaviour of AlSi7Mg Alloy Processed by Selective Laser Melting

Zahra Sajedi, Riccardo Casati, Maria Cecilia Poletti, Mateusz Skalon, Christof Sommitsch, Maurizio Vedani

Publikation: Beitrag in Buch/Bericht/KonferenzbandBeitrag in einem Konferenzband

Abstract

Heat treatable hypo-eutectic AlSi7Mg (A357) alloy is widely used for lightweight structural parts and for high temperature applications such as in cast cylinder heads.
AlSi7Mg is also a suitable alloy to be processed by selective laser melting (SLM), owing to its narrow solidification range, resistance to hot cracking and good fluidity. Employing SLM-processed parts made by AlSi7Mg in high temperature applications with cyclic thermal loads requires good resistance to thermo-mechanical fatigue due to the critical strains and stresses induced by the fluctuating temperature. In this study, the thermo-mechanical fatigue behaviour of A357 alloy samples produced by SLM has been investigated using a Gleeble®3800 simulator. A correlation has been found between the applied mechanical stress and thermo-mechanical fatigue life. Analyses on the mechanisms of failure allowed to draw conclusions about the relation between the thermo-mechanical fatigue strength and peculiar microstructure formed by SLM-processing.
Originalspracheenglisch
TitelEuro PM2019 - Congress and Exhibition
Herausgeber (Verlag)European Powder Metallurgy Association
ISBN (elektronisch)9781899072514
PublikationsstatusVeröffentlicht - 2019
VeranstaltungEuro PM2019 - Congress and Exhibition - Maastricht , Niederlande
Dauer: 13 Okt 201916 Okt 2019
https://www.europm2019.com/

Publikationsreihe

NameEuro PM 2019 Congress and Exhibition

Konferenz

KonferenzEuro PM2019 - Congress and Exhibition
LandNiederlande
OrtMaastricht
Zeitraum13/10/1916/10/19
Internetadresse

ASJC Scopus subject areas

  • !!Metals and Alloys
  • !!Surfaces, Coatings and Films
  • !!Surfaces and Interfaces

Fingerprint

Untersuchen Sie die Forschungsthemen von „Thermo-mechanical Fatigue Behaviour of AlSi7Mg Alloy Processed by Selective Laser Melting“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren