Thermally induced alloying processes in a bimetallic system at the nanoscale: AgAu sub-5 nm core-shell particles studied at atomic resolution

Maximilian Lasserus, Martin Schnedlitz, Daniel Knez, Roman Messner, Alexander Schiffmann, Florian Lackner, Andreas W. Hauser, Ferdinand Hofer, Wolfgang E. Ernst

Publikation: Beitrag in einer FachzeitschriftArtikel

Abstract

Alloying processes in nanometre-sized Ag@Au and Au@Ag core@shell particles with average radii of 2 nm are studied via high resolution Transmission Electron Microscopy (TEM) imaging on in situ heatable carbon substrates. The bimetallic clusters are synthesized in small droplets of superfluid helium under fully inert conditions. After deposition, they are monitored during a heating cycle to 600 K and subsequent cooling. The core-shell structure, a sharply defined feature of the TEM High-Angle Annular Dark-Field images taken at room temperature, begins to blur with increasing temperature and transforms into a fully mixed alloy around 573 K. This transition is studied at atomic resolution, giving insights into the alloying process with unprecedented precision. A new image-processing method is presented, which allows a measurement of the temperature-dependent diffusion constant at the nanoscale. The first quantification of this property for a bimetallic structure
Originalspracheenglisch
Seiten (von - bis)2017-2024
Seitenumfang8
FachzeitschriftNanoscale
Jahrgang10
Ausgabenummer4
DOIs
PublikationsstatusVeröffentlicht - 2018

Fields of Expertise

  • Advanced Materials Science

Dieses zitieren