Abstract
Thymine (Thy) or 2,6-diamino-1,3,5-triazine (DAT) end-groups were efficiently installed on well-defined polyethylenes (PEs) synthesized by catalyzed chain growth (CCG) polymerization. Mono- and bifunctional low-molar mass PEs (1200-1500 g·mol-1) formed lamellar morphologies with long-range order upon cooling from the melt due to microphase segregation of polar supramolecular units and apolar PE chains. Crystallization of Thy functions into rigid planes at 180 °C induced very long-range lamellar order in Thy-functionalized PEs and dramatically suppressed PE crystallization (from 67% to 19%). DAT-functionalized PEs, whose end-groups do not crystallize, showed slightly reduced PE crystallinity (62%) and less long-range order, since assembly was instead driven by PE crystallization. Mechanical analysis of the bifunctional PEs demonstrated high moduli roughly proportional to PE crystallinity but low strains at break due to the absence of chain entanglements and/or tie chains between crystalline lamellae. This work offers important insights for designing supramolecular systems with tunable thermal and mechanical properties.
Originalsprache | englisch |
---|---|
Seiten (von - bis) | 2630-2640 |
Seitenumfang | 11 |
Fachzeitschrift | Macromolecules |
Jahrgang | 51 |
Ausgabenummer | 7 |
DOIs | |
Publikationsstatus | Veröffentlicht - 10 Apr. 2018 |
ASJC Scopus subject areas
- Organische Chemie
- Polymere und Kunststoffe
- Anorganische Chemie
- Werkstoffchemie