Prediction of the mechanical and failure behavior of metal-composite hybrid joints using cohesive surfaces

Renan Pereira Alessio, Natália Manente André, Seyed M. Goushegir, Jorge F. dos Santos, José Antonio E. Mazzaferro, S. T. Amancio-Filho*

*Korrespondierende/r Autor/in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftArtikel

Abstract

Friction Spot Joining (FSpJ) is an alternative technique developed to manufacture hybrid lightweight structures by joining metal to composites. This work has developed a finite element model to evaluate the failure behavior of aluminum alloy 2024-T3 and carbon-fiber-reinforced polyphenylene sulfide single spot joints produced by FSpJ. Cohesive surface behavior was applied to model the interface between aluminum and composite in the joint. The different bonding zones of the FSpJ joint were discretized in the model with a specific traction-separation law. The numerical and experimental force versus displacement curves have presented deviations of 8% for the ultimate lap shear force (ULSF) and 1.6% for displacement at failure. The evolution of the damage in the joint occurred preferably from the free edge of the composite due to the differential stiffness between aluminum and the composite. The influence of the edge distance on the mechanical behavior of the joints was also investigated using FEM. It has been observed that longer overlap lengths redistribute the stress in the bonding area more uniformly, thereby delaying the damage evolution in the bonding zones.
Originalspracheenglisch
Aufsatznummer101205
Seitenumfang9
FachzeitschriftMaterials Today / Communications
Jahrgang24
Frühes Online-Datum20 Mai 2020
DOIs
PublikationsstatusVeröffentlicht - Sep 2020

ASJC Scopus subject areas

  • !!Mechanics of Materials
  • !!Materials Chemistry
  • !!Materials Science(all)

Fields of Expertise

  • Advanced Materials Science

Fingerprint Untersuchen Sie die Forschungsthemen von „Prediction of the mechanical and failure behavior of metal-composite hybrid joints using cohesive surfaces“. Zusammen bilden sie einen einzigartigen Fingerprint.

  • Dieses zitieren