Poly(vinyl alcohol)-based Anion Exchange Membranes for Alkaline Direct Ethanol Fuel Cells

Asep Muhamad Samsudin*, Sigrid Wolf, Michaela Roschger, Viktor Hacker

*Korrespondierende/r Autor/in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftArtikel

Abstract

Crosslinked anion exchange membranes (AEMs) made from poly(vinyl alcohol) (PVA) as a backbone polymer and different approaches to functional group introduction were prepared by means of solution casting with thermal and chemical crosslinking. Membrane characterization was performed by SEM, FTIR, and thermogravimetric analyses. The performance of AEMs was evaluated by water uptake, swelling degree, ion exchange capacity, OH- conductivity, and single cell tests. A combination of quaternized ammonium poly(vinyl alcohol) (QPVA) and poly(diallyldimethylammonium chloride) (PDDMAC) showed the highest conductivity, water uptake, and swelling among other functional group sources. The AEM with a combined mass ratio of QPVA and PDDMAC of 1:0.5 (QPV/PDD0.5) has the highest hydroxide conductivity of 54.46 mS cm-1. The single fuel cell tests with QPV/PDD0.5 membrane yield the maximum power density and current density of 8.6 mW cm-2 and 47.6 mA cm-2 at 57 °C. This study demonstrates that PVA-based AEMs have the potential for alkaline direct ethanol fuel cells (ADEFCs) application.
Originalspracheenglisch
Seiten (von - bis)435-443
Seitenumfang9
FachzeitschriftInternational Journal of Renewable Energy Development
Jahrgang10
Ausgabenummer3
DOIs
PublikationsstatusVeröffentlicht - 15 Feb 2021

ASJC Scopus subject areas

  • !!Energy Engineering and Power Technology
  • Environmental engineering
  • !!Renewable Energy, Sustainability and the Environment

Fields of Expertise

  • Mobility & Production
  • Advanced Materials Science

Fingerprint

Untersuchen Sie die Forschungsthemen von „Poly(vinyl alcohol)-based Anion Exchange Membranes for Alkaline Direct Ethanol Fuel Cells“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren