Hierarchical Metal-Organic Framework Films with Controllable Meso/Macroporosity

Renheng Bo, Mahdiar Taheri, Borui Liu, Raffaele Ricco, Hongjun Chen, Heinz Amenitsch, Zelio Fusco, Takuya Tsuzuki, Guihua Yu, Rob Ameloot, Paolo Falcaro, Antonio Tricoli*

*Korrespondierende/r Autor/-in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftArtikelBegutachtung

Abstract

The structuring of the metal-organic framework material ZIF-8 as films and membranes through the vapor-phase conversion of ZnO fractal nanoparticle networks is reported. The extrinsic porosity of the resulting materials can be tuned from 4% to 66%, and the film thickness can be controlled from 80 nm to 0.23 mm, for areas >100 cm2. Freestanding and pure metal-organic frameworks (MOF) membranes prepared this way are showcased as separators that minimize capacity fading in model Li-S batteries.

Originalspracheenglisch
Aufsatznummer2002368
FachzeitschriftAdvanced Science
Jahrgang7
Ausgabenummer24
DOIs
PublikationsstatusVeröffentlicht - 16 Dez. 2020

ASJC Scopus subject areas

  • Medizin (sonstige)
  • Chemische Verfahrenstechnik (insg.)
  • Werkstoffwissenschaften (insg.)
  • Biochemie, Genetik und Molekularbiologie (sonstige)
  • Ingenieurwesen (insg.)
  • Physik und Astronomie (insg.)

Fields of Expertise

  • Advanced Materials Science

Fingerprint

Untersuchen Sie die Forschungsthemen von „Hierarchical Metal-Organic Framework Films with Controllable Meso/Macroporosity“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren