Comparison of microstructural changes in three different Ni-base superalloys after cyclic thermo-mechanical treatment

Daniel Huber, Matthias Hacksteiner, Maria Cecilia Poletti, Fernando Warchomicka, Martin Stockinger

Publikation: Beitrag in Buch/Bericht/KonferenzbandBeitrag in einem KonferenzbandBegutachtung

Abstract

The material behavior of three Ni-base superalloys (Inconel® 718, Allvac® 718Plus™ and Haynes® 282®) during cyclic thermo-mechanical loading was investigated. Stress controlled thermo-mechanical tests were carried out at temperatures above 700 °C and different levels of maximum compressive stress using a Gleeble® 3800 testing system. Numerical precipitation kinetics simulations were performed using the software package

Originalspracheenglisch
Titel8th International Symposium on Superalloy 718 and Derivatives 2014
Herausgeber (Verlag)John Wiley & Sons, Inc
Seiten303-315
Seitenumfang13
ISBN (Print)9781634396424
PublikationsstatusVeröffentlicht - 2014
Veranstaltung8th International Symposium on Superalloy 718 and Derivatives 2014 - Pittsburgh, USA / Vereinigte Staaten
Dauer: 28 Sep. 20141 Okt. 2014

Konferenz

Konferenz8th International Symposium on Superalloy 718 and Derivatives 2014
Land/GebietUSA / Vereinigte Staaten
OrtPittsburgh
Zeitraum28/09/141/10/14

ASJC Scopus subject areas

  • Metalle und Legierungen

Fingerprint

Untersuchen Sie die Forschungsthemen von „Comparison of microstructural changes in three different Ni-base superalloys after cyclic thermo-mechanical treatment“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren