Chemical resistance of acetylated radiata pine sliced veneers

Jana Maria Joereßen, Georg Baumann, Stefan Spirk, Thomas Krenke, Thomas Schönauer, Florian Feist*

*Korrespondierende/r Autor/-in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftArtikelBegutachtung

Abstract

In an effort to increase sustainability and reduce CO2 emissions in the automotive sector, the use of renewable wood-based materials for structural elements in vehicles is gaining attention. Less durable, but locally available, wood species can be modified chemically or physically to increase their stability against degradation and make them a viable alternative to less sustainable materials even in outdoor applications. One common wood modification process is acetylation. With regard to using modified veneers in the outer layers of plywood for vehicle components, this study investigates the resistance of acetylated radiata pine veneers to automotive chemicals (distilled water, acetone, biodiesel, gasoline, anti-freeze). The specimens were exposed to the chemicals through two methods, the (1) immersion and (2) blotting paper test. Then, tensile tests were conducted to explore the influence of those chemicals on the mechanical behavior of the veneers. While in the immersion test, the highest mass increase was observed for distilled water (126 wt%), in the blotting paper test, it was found for the anti-freeze (81 wt%). In general, the acetylated veneers showed a good chemical resistance. No statistically significant influence of the chemicals on the tensile strength was observed.
Originalspracheenglisch
Seiten (von - bis)1467-1477
Seitenumfang11
FachzeitschriftWood Material Science and Engineering
Jahrgang2023
Ausgabenummer4
Frühes Online-Datum16 Dez. 2022
DOIs
PublikationsstatusElektronische Veröffentlichung vor Drucklegung. - 16 Dez. 2022

ASJC Scopus subject areas

  • Allgemeine Materialwissenschaften

Fingerprint

Untersuchen Sie die Forschungsthemen von „Chemical resistance of acetylated radiata pine sliced veneers“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren