Bainitic transformation during the two-step Q&P process in a lean medium Mn steel containing silicon

Simone Kaar, Reinhold Schneider, Daniel Krizan, Coline Beal, Christof Sommitsch

Publikation: Beitrag in Buch/Bericht/KonferenzbandBeitrag in einem Konferenzband

Abstract

Lean medium Mn Quenching and Partitioning (Q&P) steels with Mn contents up to 5 wt-% have recently gained a lot of interest due to their promising combination of strength and ductility. This steel group is characterized by a microstructure consisting of a carbon-depleted tempered martensitic (α’’) matrix and a considerable amount of retained austenite (RA) stabilized by both, C and Mn, in order to ensure a sufficient strain-induced austenite to martensite transformation (TRIP-effect). Furthermore, the hard α’’ matrix contributes to the excellent performance of these steels in bending, sheet cutting and hole expansion operations. In this contribution, the impact of the Q&P process on the transformation behavior of a 0.2C- 4.5Mn-1.5Si lean medium Mn steel is presented and discussed in detail. This includes dilatometric experiments examining the influence of the Q&P process parameters on the phase transformations, light optical and scanning electron microstructural (LOM, SEM) investigations, as well as hardness measurements according to Vickers. Moreover, the Q&P annealing approach was compared to the TRIPassisted bainitic ferrite (TBF) process, in order to evaluate the influence of primary martensite (α’initial) being present in the Q&P samples at the onset of isothermal bainitic transformation (IBT) on the transformation kinetics. With increasing quench temperature (TQ) the amount of α’’ significantly decreased, whereas the phase fraction of bainitic ferrite (αB) and RA continuously increased, leading to the formation of fresh martensite (α’final) and the sharp decrease of the RA fraction at TQ exceeding 250°C. Furthermore, with increasing partitioning temperature (TP) a decreasing amount of αB, associated with an increasing amount of α’final, could be examined. The comparison of the Q&P and TBF process in terms of transformation behavior manifested a pronounced influence of the presence of α’initial, since the IBT was intensively accelerated in the Q&P samples.
Originalspracheenglisch
TitelEuropean Conference on Heat Treatment ECHT 2019
PublikationsstatusVeröffentlicht - 2019
VeranstaltungEuropean Conference on Heat Treatment 2019 - Bardolino, Bardolino, Italien
Dauer: 5 Jun 20197 Jun 2019

Konferenz

KonferenzEuropean Conference on Heat Treatment 2019
KurztitelECHT 2019 Conference
LandItalien
OrtBardolino
Zeitraum5/06/197/06/19

ASJC Scopus subject areas

  • !!Materials Science (miscellaneous)

Fields of Expertise

  • Advanced Materials Science

Fingerprint Untersuchen Sie die Forschungsthemen von „Bainitic transformation during the two-step Q&P process in a lean medium Mn steel containing silicon“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren