Ageing of al-mn-cu-be alloys for stimulating precipitation of icosahedral quasicrystals

Tonica Bončina*, Mihaela Albu, Franc Zupanič

*Korrespondierende/r Autor/in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftArtikel

Abstract

In this work, the ageing of some Al-Mn-Cu-Be alloys was investigated in the temperature range in which predominantly icosahedral quasicrystalline (IQC) precipitates can form. The alloys were cast into a copper mould, directly aged (T5 heat treatment) between 300 and 440 C for different times. Afterwards, they were examined using scanning and transmission electron microscopy, X-ray diffraction and hardness testing. The main aim of the work was to determine the conditions at which a high number density of spherical icosahedral quasicrystalline precipitates can form. The highest number density of IQC precipitates was obtained at 300 C after prolonged ageing. The spheroidal precipitates had a diameter less than 20 nm. The size of IQC precipitates increased with the increasing temperature, and in addition, decagonal quasicrystalline precipitates appeared. The time to maximum hardness decreased strongly with increasing ageing temperature. The IQC precipitates can form in a fairly broad temperature range in Al-Mn-Cu-Be alloys and that by varying ageing temperature and duration, rather different distributions of precipitates can be obtained. The presence of precipitates caused rather strong aluminium alloys and fast work hardening during initial plastic deformation.

Originalspracheenglisch
Aufsatznummer937
Seiten (von - bis)1-16
Seitenumfang16
FachzeitschriftMetals
Jahrgang10
Ausgabenummer7
DOIs
PublikationsstatusVeröffentlicht - 1 Jan 2020

ASJC Scopus subject areas

  • !!Materials Science(all)

Fingerprint Untersuchen Sie die Forschungsthemen von „Ageing of al-mn-cu-be alloys for stimulating precipitation of icosahedral quasicrystals“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren